ʻIkepili Huahana:
ʻO 191 kahi ʻano DCPD pre accelerated unsaturated polyester resin me ka viscosity haʻahaʻa a me ke kiʻekiʻe reactivity, nā waiwai mechanical maikaʻi, loaʻa kekahi kūpaʻa corrosion, kūpono no nā huahana FRP maʻamau.
ʻIkepili ʻenehana o Liquid Resin | |||
'ikamu | Unite | Waiwai | Kūlana |
Ka nana aku | ʻO ka wai mānoanoa mānoanoa | Nānā | |
Waiwai ʻakika | mgKOH/g | 16-23 | GB2895-82 |
Viscosity(25 ℃) | mPa.S | 350-550 | GB7193.1-87 |
Manawa Gel | min | 3-10 | GB7193.6-87 |
ʻAʻole-Volatile | % | 68-73 | GB7193.3-87 |
Nānā: ʻO ka manawa Gel he 25 ° C;i ka ʻauʻau hau;0.5ml kobalt isocaprylate solutiona me 0.5 ml MEKP i hoʻohui ʻia i loko o 50 g resin |
Nā Papa kuhikuhi hana o ka mea hoolei resin | |||
'ikamu | Unite | Waiwai | Kūlana |
ʻO ka paʻakikī Barcol≥ | Barcol | 40 | GB3854-1983 |
Ka ikaika tensile ≥ | MPa | 55 | GB2568-1995 |
ʻO ka modulus tensile ≥ | MPa | 3000 | GB2568-1995 |
ʻO ka hoʻolōʻihi ʻia i ka wā hoʻomaha≥ | % | 3.0 | GB2568-1995 |
Ka ikaika wili≥ | MPa | 80 | GB2570-1995 |
Pākuʻi hoʻololi≥ | MPa | 3200 | GB2570-1995 |
Ka ikaika hopena≥ | KJ/m2 | 6 | GB2571-1995 |
HDT ≥ | ℃ | 70 | GB1634-1989 |
Nānā: Ka Mahana Kaiapuni no ka hoʻokolohua: 23±2 °C;haʻahaʻa pili: 50±5% |