I-Orthophthalic noma i-DCPD I-polyester Engasetshenzisiwe Yokubeka Isandla Phezulu 191 196
Ulwazi Lomkhiqizo:
I-191 iwuhlobo lwe-DCPD pre accelerated polyester unsaturated resin ene-viscosity emaphakathi kanye nokusebenza kabusha okuphezulu, izakhiwo ezinhle zomshini, inokumelana nokugqwala okuthile, ifanele imikhiqizo ye-FRP yokubeka izandla evamile.
Izinkomba Zobuchwepheshe ze-Liquid Resin | |||
Into | Iyunithi | Inani | Okujwayelekile |
Ukubukeka | I-Transparent Sticky Thick Liquid | Okubonakalayo | |
I-Acid Value | mgKOH/g | 16-23 | I-GB2895-82 |
I-Viscosity(25℃) | mPa.S | 350-550 | I-GB7193.1-87 |
Isikhathi se-Gel | imiz | 3-10 | I-GB7193.6-87 |
Okungaguquguquki | % | 68-73 | I-GB7193.3-87 |
Qaphela: Isikhathi seGel singu-25°C;ekugezeni umoya;0.5ml isixazululo se-cobalt isocaprylatekanye nesisombululo se-MEKP esingu-0.5 ml sengezwe ku-50 g resin |
Izinkomba zokusebenza ze-Resin Casting Substance | |||
Into | Iyunithi | Inani | Okujwayelekile |
Ukuqina kweBarcol≥ | Barcol | 40 | GB3854-1983 |
Amandla okuqina ≥ | I-MPa | 55 | I-GB2568-1995 |
I-tensile modulus ≥ | I-MPa | 3000 | I-GB2568-1995 |
Ukwandisa ngesikhathi sekhefu≥ | % | 3.0 | I-GB2568-1995 |
Amandla e-Flexural≥ | I-MPa | 80 | I-GB2570-1995 |
I-Flexural modulus≥ | I-MPa | 3200 | I-GB2570-1995 |
Amandla omthelela≥ | KJ/m2 | 6 | I-GB2571-1995 |
I-HDT ≥ | ℃ | 70 | I-GB1634-1989 |
Qaphela: Izinga Lokushisa Lendawo Yokulinga: 23±2°C;umswakama ohlobene: 50±5% |
Ukupakisha Nokugcina:
191: Ipakishwe ebhakedeni lensimbi lama-220 KG wesisindo senetha neshalofu yokuphila kwezinyanga eziyisi-6 ku-20°C ezindaweni ezingenawo umoya;ukugwema ukukhanya kwelanga nokushisa noma umlilo.
Qaphela: Idatha ihlolwe ngokwezinga le-GB.Bethonywe izici eziningi ohlelweni lokwenziwa, ucwaningo oludingekayo olwenziwe ngabasebenzisi alukhethekile.Ngokomthetho, azikho iziqinisekiso zemisebenzi ethile yomkhiqizo ezisebenza ekusetshenzisweni okukodwa, futhi amalungelo okuchibiyela okokusebenza agodliwe.