I-Orthophthalic okanye i-DCPD ipolyester engafakwanga yoKubeka isandla Phezulu 191 196
Ulwazi ngeMveliso:
I-191 luhlobo lwe-DCPD olukhawulezayo lwe-polyester engaxutywanga kunye ne-viscosity ephakathi kunye ne-reactivity ephezulu, iipropathi ezilungileyo zoomatshini, zinokuxhathisa okuthile ku-corrosion, zilungele iimveliso ze-FRP eziqhelekileyo zokubeka izandla.
Izalathisi zobuGcisa beResin engamanzi | |||
Into | Iyunithi | Ixabiso | Umgangatho |
Imbonakalo | Ulwelo oluNcangathi oluNcangathi oluNgaphandle | Okubonakalayo | |
Ixabiso le-Acid | mgKOH/g | 16-23 | GB2895-82 |
Viscosity(25℃) | mPa.S | 350-550 | GB7193.1-87 |
Ixesha leGel | imiz | 3-10 | GB7193.6-87 |
Ukungaguquguquki | % | 68-73 | GB7193.3-87 |
Qaphela: Ixesha leGel ngu-25 ° C;kwindawo yokuhlambela emoyeni;I-0.5ml isisombululo se-cobalt isocaprylatekunye ne-0.5 ml isisombululo se-MEKP zongezwa kwi-50 g resin |
Izalathisi zokusebenza zeResin Casting Substance | |||
Into | Iyunithi | Ixabiso | Umgangatho |
Barcol hardness≥ | Barcol | 40 | GB3854-1983 |
Amandla okuqina ≥ | MPa | 55 | GB2568-1995 |
Imodyuli yokuqina ≥ | MPa | 3000 | GB2568-1995 |
Ukwandiswa ngexesha lekhefu≥ | % | 3.0 | GB2568-1995 |
Amandla e-Flexural≥ | MPa | 80 | GB2570-1995 |
Flexural modulus≥ | MPa | 3200 | GB2570-1995 |
Amandla empembelelo≥ | KJ/m2 | 6 | GB2571-1995 |
HDT ≥ | ℃ | 70 | GB1634-1989 |
Qaphela: Ubushushu beNdawo kuMvavanyo: 23±2°C;ukufuma okuhambelanayo: 50±5% |
Ukupakisha kunye nokugcina:
I-191: Ifakwe kwi-pail yensimbi ye-220 KG ubunzima obunetha kunye neshelufu yeenyanga ze-6 kwi-20 ° C kwiindawo ezinomoya;ukuphepha ukukhanya kwelanga kunye nobushushu okanye umlilo.
Qaphela: Idatha yavavanywa ngokwemigangatho ye-GB.Ukuphenjelelwa zizinto ezininzi kwinkqubo yokwenziwa, uphando oluyimfuneko ngabasebenzisi alukhethekile.Ngokomthetho, akukho ziqinisekiso zentsebenzo ethile yemveliso esebenzayo kusetyenziso oluthile oluthile, kwaye amalungelo okulungisa izinto agciniwe.