Polyester ea Orthophthalic kapa DCPD Unsaturated bakeng sa ho Beha Matsoho 191 196
Lintlha tsa Sehlahisoa:
191 ke mofuta oa DCPD pre accelerated unsaturated polyester resin e nang le viscosity e itekanetseng le reactivity e phahameng, thepa e ntle ea mochine, e na le khanyetso e itseng ea kutu, e loketseng lihlahisoa tse tloaelehileng tsa FRP tsa matsoho.
| Litlhaloso tsa Tekheniki tsa Resin ea Metsi | |||
| Ntho | Yuniti | Boleng | Standard |
| Ponahalo | Mokelikeli o Motenya oa Transparent Sticky | E bonoang | |
| Boleng ba Asiti | mgKOH/g | 16-23 | GB2895-82 |
| Viscosity(25℃) | mPa.S | 350-550 | GB7193.1-87 |
| Nako ea Gel | min | 3-10 | GB7193.6-87 |
| E sa Feleng | % | 68-73 | GB7193.3-87 |
| Tlhokomeliso: Nako ea Gel ke 25 ° C;ka bateng ea moea;0.5ml tharollo ea cobalt isocaprylatele 0.5 ml tharollo ea MEKP e kenyelelitsoe ka 50 g resin | |||
| Litlhaloso tsa Ts'ebetso ea Resin Casting Substance | |||
| Ntho | Yuniti | Boleng | Standard |
| Barcol hardness≥ | Barcol | 40 | GB3854-1983 |
| Matla a tsitsitseng ≥ | MPa | 55 | GB2568-1995 |
| Tensile modulus ≥ | MPa | 3000 | GB2568-1995 |
| Elongation nakong ea khefu≥ | % | 3.0 | GB2568-1995 |
| Flexural matla≥ | MPa | 80 | GB2570-1995 |
| Flexural modulus≥ | MPa | 3200 | GB2570-1995 |
| Matla a tshusumetso≥ | KJ/m2 | 6 | GB2571-1995 |
| HDT ≥ | ℃ | 70 | GB1634-1989 |
| Tlhokomeliso: Mocheso oa Tikoloho bakeng sa Teko: 23±2°C;mongobo o lekanyelitsoeng: 50±5% | |||
Ho paka le ho Boloka:
191: E phuthetsoe ka sekoting sa tšepe sa 220 KG boima ba net le bophelo ba sethala sa likhoeli tse 6 ho 20 ° C libakeng tse nang le moea oa moea;ho qoba kganya ya letsatsi le mocheso kapa mollo.
Tlhokomeliso: Lintlha li ile tsa lekoa ho latela maemo a GB.E susumetsoa ke lintlha tse ngata ts'ebetsong ea tlhahiso, liphuputso tse hlokahalang ke basebelisi ha lia ikhetha.Ka molao, ha ho na waranti bakeng sa ts'ebetso e itseng ea sehlahisoa e sebetsang ts'ebelisong e le 'ngoe e khethehileng,' me litokelo tsa ho lokisa thepa li bolokiloe.