Orthophthalic ma ọ bụ DCPD Unsaturated polyester for Hand Lay Up 191 196
Ozi ngwaahịa:
191 bụ ụdị DCPD pre accelerated unsaturated polyester resin na agafeghị oke viscosity na elu reactivity, ezi n'ibu Njirimara, nwere ụfọdụ corrosion eguzogide, adabara nkịtị aka nkịtị-elu FRP ngwaahịa.
Nka nka nka nke Resin Liquid | |||
Ihe | Nkeji | Uru | Ọkọlọtọ |
Ọdịdị | Mmiri mmiri na-egbuke egbuke | Anya | |
Uru acid | mgKOH/g | 16-23 | GB2895-82 |
Viscosity (25 ℃) | mPa.S | 350-550 | GB7193.1-87 |
Gel oge | min | 3-10 | GB7193.6-87 |
Na-adịghị agbanwe agbanwe | % | 68-73 | GB7193.3-87 |
Rịba ama: Gel Oge bụ 25 ° C;na ikuku bat;0.5ml cobalt isocaprylate ngwọtana 0,5 ml MEKP ngwọta na-agbakwunyere n'ime 50 g resin |
Ndekọ arụmọrụ nke ihe nkedo resin | |||
Ihe | Nkeji | Uru | Ọkọlọtọ |
Barcol hardness ≥ | Barcol | 40 | GB3854-1983 |
Ike tensile ≥ | MPa | 55 | GB2568-1995 |
modul tensile ≥ | MPa | 3000 | GB2568-1995 |
Elongation na nkwụsịtụ ≥ | % | 3.0 | GB2568-1995 |
Ike mgbanwe ≥ | MPa | 80 | GB2570-1995 |
Ụdị mgbanwe mgbanwe ≥ | MPa | 3200 | GB2570-1995 |
Ike mmetụta≥ | KJ/m2 | 6 | GB2571-1995 |
HDT ≥ | ℃ | 70 | GB1634-1989 |
Rịba ama: Okpomọkụ gburugburu ebe obibi maka nnwale: 23 ± 2 ° C;iru iru mmiri: 50± 5% |
Mbukota na Nchekwa:
191: Ejiri ya na pail metal nke 220 KG net arọ na ndụ nchekwa nke ọnwa 6 na 20 Celsius na ebe ikuku;na-ezere ìhè anyanwụ kpọmkwem na okpomọkụ ma ọ bụ ọkụ.
Mara: A nwalere data a dịka ọkọlọtọ GB siri dị.N'ịbụ ndị na-emetụta ọtụtụ ihe na usoro mmepụta ihe, nchọpụta ndị dị mkpa site n'aka onye ọrụ abụghị nanị.N'ụzọ iwu kwadoro, ọ nweghị akwụkwọ ikike maka ụfọdụ arụmọrụ nke ngwaahịa na-adabara maka otu ojiji, yana ikike imezi ihe ndị a ka edobere.